产品参数Product Parameter类   型CATAGORY型号TYPE组   成CONTENT 电化学活性面积ECSA 粒   径SIZE 铂黑催化剂 Pt blackHiCaP100>95wt.% Pt 40 m²/g 5.6 nm *催化剂载量、颗径大小、组成等可按客户要求定制。HiCaP100◆    单批次>800克规模化制备，且一致性好；         Preparation of one batch >800 gram with good consistency;◆    粒径小、分散度高且稳定性好：平均粒径约为5.6nm；         Small particle size, high dispersion and good durability: the average particle size is about ca. 5.6nm;◆    极好的耐久性，20000圈循环后其ECSA下降约5%，质量比活性下降约5%         After 20K cycles, the ECSA reduced by about 5%， the mass activity reduced by about 5%; ◆    膜电极性能优良：65oC时氢/氧燃料电池膜电极功率密度可达1.8 Wcm-2@0.6V。        The power density of H2-O2 PEMFC at 75oC is 1.8 Wcm-2@0.6V 。

产品参数Product Parameter类   型CATAGORY型  号TYPE组   成CONTENT 电化学活性面积ECSA粒  径SIZE 铱黑催化剂 IrHiCaI100>95wt.% Ir53 m²/g4.5 nmHiCaI100◆    单批次>1000克规模化制备，且一致性好；         Preparation of one batch >1000 gram with good consistency;◆    粒径小、分散度高且稳定性好：平均粒径约为4.5nm；         Small particle size, high dispersion and good durability: the average particle size is about ca. 4.5nm;◆    氧析出过点位315mV@10mA/cm2         The overpotential is 315mV@10mA/cm2 for OER◆    电压1.72V@1A/cm2,1.93V@2A/cm2;经过8000小时长时间测试，性能无衰减。       The potential is 1.72V@1A/cm2，1.93V@2A/cm2；and after 8000h text， no obvious degradation is shown.

产品参数Product Parameter类   型CATAGORY型  号TYPE组   成CONTENT 电化学活性面积ECSA粒  径SIZE 氧化铱催化剂 IrO2 HiCaIO100>95wt.% IrO225 m²/g7.5 nm*催化剂载量、颗径大小、组成等可按客户要求定制。HiCaIO100◆    单批次>1000克规模化制备，且一致性好；         Preparation of one batch >1000 gram with good consistency;◆    粒径小、分散度高且稳定性好：平均粒径约为7.5nm；         Small particle size, high dispersion and good durability: the average particle size is about ca. 7.5nm;◆    氧析出过点位319mV@10mA/cm2         The overpotential is 319mV@10mA/cm2 for OER◆    电压1.72V@1A/cm2,1.89V@2A/cm2;经过8000小时长时间测试，性能无衰减。       The potential is 1.72V@1A/cm2，1.89V@2A/cm2；and after 8000h text， no obvious degradation is shown.

产品参数Product Parameter类 型 CATAGORY型 号 TYPE组 成 CONTENT电化学活性面积ECSA粒 径 SIZE钯碳催化剂Pd/CHiCaPd2020wt.%Pd，80wt.%C112m²/g3.8nmHiCaPd4040wt.% Pd，60wt.%C65m²/g4.6nm催化剂载量、颗径大小、组成等可按客户要求定制。

产品参数Product Parameter类   型CATAGORY型号TYPE组   成CONTENT电化学活性面积     ECSA粒   径SIZE 铂碳催化剂Pt/CHiCaP4040wt.% Pt,60wt.%C95 m2/g2.8 nmHiCaP6060wt.% Pt,40wt.%C90 m2/g3.1 nm HiCaP7070wt.% Pt,30wt.%C55 m2/g3.3nm HiCaP40◆    单批次>1000克规模化制备，且一致性好；         Preparation of one batch >1000 gram with good consistency;◆    粒径小、分散度高且稳定性好：平均粒径约为2.8nm；         Small particle size, high dispersion and good durability: the average particle size is about ca. 2.8nm;◆    极好的耐久性，20000圈循环后其ECSA下降约5%，质量比活性下降约5%         After 20K cycles, the ECSA reduced by about 5%， the mass activity reduced by about 5%; ◆    膜电极性能优良：75oC时氢/空燃料电池膜电极功率密度可达1.24 Wcm-2@0.62V。        The power density of H2-Air PEMFC at 75oC is 1.24 Wcm-2@0.62V 。HiCaP60◆    单批次>1000克规模化制备，且一致性好；         Preparation of one batch >1000 gram with good consistency;◆    粒径小、分散度高且稳定性好：平均粒径约为3.1nm；         Small particle size, high dispersion and good durability: the average particle size is about ca.3.1 nm;◆    长时间耐久性好，20000圈循环后其ECSA下降约5%，质量比活性下降约5%        After 20K cycles, the ECSA reduced by about 5%， the mass activity reduced about 5%; ◆    膜电极性能优良：65oC时氢/空燃料电池膜电极功率密度可达1 .2Wcm-2@0.62V。        The power density of H2-Air PEMFC at 65oC is 1.2Wcm-2@0.62V 。 HiCaP70◆    单批次>1000克规模化制备，合金化程度高；         Preparation of one batch >1000gram with high degree of alloy;◆    粒径小、分散度高且稳定性好：平均粒径约为3.3 nm；         Small particle size, high dispersion and good durability: the average particle size is about ca.3.3nm;◆     膜电极性能优良：65oC时氢/空燃料电池膜电极功率密度可达1 .2Wcm-2@0.62V。          The power density of H2-Air PEMFC at 65oC is 1.2Wcm-2@0.62V 。*催化剂载量、颗径大小、组成等可按客户要求定制。铂碳催化剂是将铂负载到活性炭上的一种载体催化剂，主要用于燃料电池的氢气氧化、甲醇氧化、甲酸氧化以及氧气的还原等化学反应，属于十分常见的贵金属催化剂。

产品参数Product Parameter类   型CATAGORY型号TYPE组   成CONTENT电化学活性面积 ECSA粒   径SIZE 铂钌碳催化剂 PtRu/CHiCaPR6040 wt.% Pt, 20wt.% Ru, 40wt.% C40 m²/g4.0nm HiCaPR60◆    单批次>1000克规模化制备，合金化程度高；         Preparation of one batch >1000 gram with high degree of alloy;◆    粒径小、分散度高且稳定性好：平均粒径约为2.6 nm；         Small particle size, high dispersion and good durability: the average particle size is about ca.2.6nm;◆    适用于直接甲醇燃料电池阳极、抗毒化电极等。        It is suitable for the anode of DMFC, anti-toxic electrode,etc.  *催化剂载量、颗径大小、组成等可按客户要求定制。

  产品参数Product Parameter 类   型CATAGORY型  号TYPE组   成CONTENT 电化学活性面积ECSA 粒   径SIZE 铂钌黑催化剂PtRuHiCaPR10065wt.%Pt, 35wt.% Ru76m²/g3.2 nm催化剂载量、颗径大小、组成等可按客户要求定制。